Firing conditions and properties of the Roman Period grey ceramics

Dobrzańska, Halina; Kielski, Andrzej; Wodnicka, Krystyna

doi:0066-5924

Obiekt planowany

Tytuł: Firing conditions and properties of the Roman Period grey ceramics

Abstrakt:

Properties of the archeological ceramics of the Late Roman Period from Zofipole near Cracow (Poland), were tested as well as raw material samples made from potential sources and fired in the laboratory kiln in oxidising and reducing atmospheres. Density, bulk density, porosity, specific surface area BET, DTA, DTG and ultrasonic wave speed were measured. It was stated that properties of the samples fired in reducing atmosphere were slightly better in comparison with oxidising one. The main reason of grey colour of the Roman Period ceramics is carbon residue as the result of relatively high content of the organic matter in the clayey materials and reducing firing conditions. In the Roman times grey ceramics was most popular in Central and Eastern Europe, while the red one in the Mediterranean area. The main reasons of this phenomenon were local cultural traditions supported by abundance of clayey materials with relatively high content of organic matter, simplicity of firing process in reducing atmosphere at low temperatures, and better properties of the vessels

Bibliografia:

Dobrzańska, H. (ed.) 1999. Zagadnienie wytwórczości garncarskiej na terenie środkowoeuropejskiej części Barbaricum w okresie rzymskim – przypadek Zofipola (Typescript of the project report for the Polish Committee of Scientific Research)
Dobrzańska, H. and T. Kalicki 2009. Zaplecze surowcowe dla osadnictwa z okresu rzymskiego w okolicach Krakowa. In Księga pamiątkowa Profesora Stanisława Pazdy, A. Błażejewski (ed.). In print
Dobrzańska, H., A. Kielski and K. Wodnicka 2006. Archeologiczna ceramika „siwa” na przykładzie Zofipola. Materiały Ceramiczne 58 (1): 35–9
Dušek, S., H. Hohmann, W. Müller and W. Schmidt 1986. Haarhausen I – Rekonstruktion eines Töpferofens und des Brennverfahrens, Weimarer Monographien zur Ur- und Frühgeschichte 16
Fabbri, B., S. Gualtieri S. and S. Santoro 2002. The importance of the firing atmosphere in the production of coarse ceramics with calcite and chamotte inclusions. In Materials of 31th Symposium on Archaeometry, Archaeometry 98, BAR International Series 1043(I): 191–5
Goerlich, E., L. Muszyński and J. Rodak 2005. Eksperymentalny wypał naczyń glinianych i jego efekty, In Experimentálna archeológia a popularizácia archeologického bádania v múzejnej a školskej praxi, M. Kotorová- Jenčová (ed.), 63–71. Hanušovce nad Topl’ou
Kociszewski, L. and J. Kruppé 1973. Badania fizykochemiczne ceramiki warszawskiej XIV–XVII wieku. Warszawa. Studia i materiały z historii kultury materialnej 47
Pawlikowski, M. 1999. Badania laboratoryjne materiałów ceramicznych z Zofipola. In H. Dobrzańska (ed.) 1999: 18–40
Rice, P.M. 1987. Pottery analysis. A sourcebook. Chicago-London
Rye, O.S. 1981. Pottery technology. Principles and reconstruction. Manuals on Archeology 4. Washington
Wodnicka, K. and A. Kielski 1997. Przemiany termiczne mas porcelanowych i fajansowych w świetle zmian powierzchni właściwej. Szkło i Ceramika 48: 25–30